PC/ABS LUPOY EF5001RFT
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, EU Eco-Label compliant
Application: Display housing
CAS: and
Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19g/cc | 1.19g/cc | ASTM D792 |
| Maximum Moisture Content | 0.040 | 0.040 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040-0.0080cm/cm @Thickness 3.20 mm | 0.0040-0.0080in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 20g/10 min @Load 2.16 kg, Temperature 250 °C | 20g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 56.9MPa @Thickness 3.20 mm | 8250psi @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm | 30 % @Thickness 0.126 in | 50mm/min; ASTM D638 |
| Flexural Yield Strength | 93.2MPa @Thickness 3.20 mm | 13500psi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| Flexural Modulus | 2.45GPa @Thickness 3.20 mm | 356ksi @Thickness 0.126 in | 10mm/min; ASTM D790 |
| Izod Impact, Notched | =4.90J/cm @Thickness 3.20 mm, Temperature 23.0 °C | =9.18ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
PC/ABS LUPOY EF5001RFT
简介
ABS工程塑料即PC ABS（工程塑料合金），在化工业的中文名字叫塑料合金，之所以命名为PC ABS，是因为这种材料既具有PC树脂的优良耐热耐候性、尺寸稳定性和耐冲击性能，又具有ABS树脂优良的加工流动性。
所以应用在薄壁及复杂形状制品，能保持其优异的性能，以及保持塑料与一种酯组成的材料的成型性。
ABS工程塑料大的缺点就是质量重、导热性能欠佳。
它的成型温度取于它们两者原料的之间温度，就是240-265度，温度太高ABS会分解，太低PC料的流动性不良。